Investigation of Cu-poor and Cu-rich Cu(In,Ga)Se-2/CdS interfaces using hard X-ray photoelectron spectroscopy


Creative Commons License

Uemsuer B., Calvet W., Hoepfner B., Steigert A., Lauermann I., Gorgoi M., ...Daha Fazla

THIN SOLID FILMS, cilt.582, ss.366-370, 2015 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 582
  • Basım Tarihi: 2015
  • Doi Numarası: 10.1016/j.tsf.2014.08.049
  • Dergi Adı: THIN SOLID FILMS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.366-370
  • Anahtar Kelimeler: Chalcopyrite, Hard X-ray photoelectron spectroscopy, Cd diffusion, Interface, ANGULAR-DISTRIBUTION PARAMETERS, SOLAR-CELLS, THIN-FILMS, CD, DIFFUSION, DEPLETION
  • Yozgat Bozok Üniversitesi Adresli: Hayır

Özet

Cu-poor and Cu-rich Cu(In,Ga)Se-2 (CIGSe) absorbers were used as substrates for the chemical bath deposition of ultrathin CdS buffer layers in the thickness range of a few nanometers in order to make the CIGSe/CdS interface accessible by hard X-ray photo-emission spectroscopy. The composition of both, the absorber and the buffer layer as well as the energetics of the interface was investigated at room temperature and after heating the samples to elevated temperatures (200 degrees C, 300 degrees C and 400 degrees C). It was found that the amount of Cd after the heating treatment depends on the near surface composition of the CIGSe absorber. No Cd was detected on the Cu-poor surface after the 400 degrees C treatment due to its diffusion into the CIGSe layer. In contrast, Cd was still present on the Cu-rich surface after the same treatment at 400 degrees C. (C) 2014 Elsevier B.V. All rights reserved.