Boron Nitride-Modified Hemp Nanofiber Reinforced Slag-Based Geopolymer Composites: Mechanical, Microstructural and Fire Resistance Performance

Filazi A., Tezcan İ. M., Akat R., Doğan D., Erdem Ü.

Polymers, cilt.18, sa.11, 2026 (SCI-Expanded, Scopus) identifier identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 18 Sayı: 11
  • Basım Tarihi: 2026
  • Doi Numarası: 10.3390/polym18111288
  • Dergi Adı: Polymers
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Chemical Abstracts Core, Compendex, INSPEC, Academic Search Ultimate (EBSCO), Engineering Source (EBSCO), Materials Science & Engineering Collection (ProQuest), Technology Collection (ProQuest)
  • Anahtar Kelimeler: boron nitride, electrospinning, fire resistance, geopolymer, GGBFS, hemp fiber, nanocomposite, SDG 11, SDG 12, SDG 9, sustainable material
  • Yozgat Bozok Üniversitesi Adresli: Evet

Özet

This study investigates the mechanical performance, high-temperature resistance, and microstructural characteristics of ground granulated blast furnace slag (GGBFS)-based geopolymer composites reinforced with boron nitride (BN)-modified hemp nanofibers. BN-modified hemp nanofibers (PVA-mBN/Hemp) were produced via electrospinning and incorporated into geopolymer mixtures at varying ratios ranging from 0 to 4 wt%. The effects of nanofiber content on composite properties were evaluated through mechanical testing, ultrasonic pulse velocity (UPV) measurements, and exposure to elevated temperatures (300–1200 °C), supported by SEM-EDS, FTIR, and XRD analyses. The results indicate that low nanofiber additions (0.5–1 wt%) improve flexural strength by up to 15%, although compressive strength is slightly reduced due to increased porosity. UPV measurements confirm the changes in internal structure. At elevated temperatures, nanofiber-reinforced samples exhibit enhanced residual strength compared to the control specimens, particularly at moderate temperatures, whereas significant degradation occurs above 900 °C. Microstructural analyses reveal improved fiber-matrix interaction, reduced crack propagation, and enhanced thermal stability attributed to BN modification. Overall, the incorporation of 0.5–1 wt% BN-modified hemp nanofibers provides an effective balance between mechanical performance and high-temperature resistance, highlighting their potential for use in sustainable and fire-resistant construction materials. This study contributes to the United Nations Sustainable Development Goals (SDGs), particularly SDG 9 (Industry, Innovation, and Infrastructure), SDG 11 (Sustainable Cities and Communities), and SDG 12 (Responsible Consumption and Production).